NEOPARIES PANELS

Innovision Solutions is an authorised supplier of Neoparies Crystalised Glass Panels.

Neoparies panels can be used for interior and exterior wall cladding applications.

A Triumph of Modern Glass Technology Weight/Strength NEOPARIES is lighter and stronger than granite and more resistant to scratching and abrasion than marble. They are not subject to the fissure and fracture patterns that commonly result from the quarrying of stone. With a greater bending strength, they can fabricated into thinner panels than natural stone. Easily Formed into Curved Panels NEOPARIES can be re-formed into a wide range of convex and concave radii panels, resulting in greater design flexibility at lower cost than hewn stone. Impermeability/Minimum Maintenance NEOPARIES is virtually impermeable and are not subject to freeze-thaw damage, penetration by rust, mortar or other staining substances. Moisture absorption, as a design consideration, has been eliminated. With NEOPARIES, contaminants are easily removed during regular building maintenance. Even graffiti can be cleaned without difficulties. Low Thermal Expansion With an extremely low coefficient of expansion, NEOPARIES is not subject to thermal cracking that can affect other cladding materials. Weather Resistance NEOPARIES is significantly more resistant to acids, alkalis, oils and other chemical substances than either marble or granite. Unlike stone, their surface and physical properties are not degraded even after years of exposure to environmental pollutants, including acid rain. Properties (Neoparies, Marble, Granite)   Neoparies(white) Marble Granite LIGHTING Diffuse reflection rate [%] 80 42 44 Regular reflection rate [%] 4 4 4 THERMAL Thermal expansion coefficient(30 - 380oC) [X10-6/K] 6.1 7.0 7.0 Thermal conductivity [W/(m * K)] 1.6 2.3 2.1 Specific heat [J/(kg * K)] 710 750 750 MECHANICAL Specific gravity   2.7 2.7 2.7 Bending strength [N/mm2] 41 11 14 Young's modulus [x104N/mm2] 8.6 7.5 5.1 Mohs' hardness   5.5 3 5.5 CHEMICAL Acid resistance*1 [mg/cm2] 0.2 267 26.2 Alkali resistance*2 [mg/cm2] 0.7 7.8 2.6 Seawater resistance*3 [mg/cm2] 0.1 0.2 0.2 Water absorption rate*4 [%] 0.0 0.3 0.4 Freeze resistance*5 [%] 0.0 0.2 0.3 Notes *1 Weight loss of test pieces of 25x25x5mm after 24-hour immersion in 1% H2SO4 solution of 90oC. *2 Weight loss of test pieces of 25x25x5mm after 24-hour immersion in 1% NaOH solution of 90oC. *3 Weight loss of test pieces of 25x25x5mm after 24-hour immersion in 1% simulated seawater of 90oC. *4 Weight increasing rate of test piece of 25x25x15mm after 48-hour immersion in water. *5 Weight loss of test pieces of 15x15x10mm after 25 cycles: immersion of test piese in water of 25oC for 2 days = expose for 4 hours in a temperature of -20oC. * The figures of the properties in this table are measured values, not guaranteed. The guaranteed values are available upon your request. Colour Variation NEOPARIES Colours New White Colour NEOPARIES AXIA Colour Variation Table of Standard Size and Standard Radius NEOPARIES Standard Size Flat Panel 900 x 900 x 15t 900 x 1800 x 15t (MAX) Curved Panel 900 x 1200 x 15t (MAX) NEOPARIES Standard Radius Convex 300R 700R 1800R 350R 750R 2000R 400R 800R 2500R 450R 900R 3000R 500R 1000R 3500R 550R 1200R 4000R 600R 1400R 650R 1600R Concave 350R 1200R 2500R 550R 1400R 3000R 750R 1600R 4000R 1000R 2000R